Utilizziamo cookie per assicurarti una migliore esperienza sul sito. Utilizziamo cookie di parti terze per inviarti messaggi promozionali personalizzati. Per maggiori informazioni sui cookie e sulla loro disabilitazione consulta la Cookie Policy. Se prosegui nella navigazione acconsenti all’utilizzo dei cookie.
 

AMOTHERM STEEL TOP SB

Protective solvent-based vinyl topcoat for intumescent coatings on steel

Solvent-based vinyl topcoat for the protection of AMOTHERM STEEL intumescent paint coatings. Recommended for particular decorative needs in indoor and semi-exposed outdoor environments.
 
CARATTERISTICHE E MODALITÁ D’USO
Pennello
Spruzzo
 
 
Informazioni sul prodotto

Technical features

  • Makes the film resistant to condensation, damp and water
  • Can be used to obtain coloured effects indoors but above all for protecting coatings in semi-exposed outdoor environments
  • Single component

 

Applications

The ideal solution for the protection of AMOTHERM STEEL SB intumescent paint coatings, giving them extra resistance in semi-exposed environments (sheds) or in humid atmospheres.

 

Drying time

  • 2 hours at surface
  • 24 – 48 hours at depth

 

Consumption

Interior: 150 g/m2 (120μm of wet film, 60μm of dry film)

Outdoors: about 250 g/m2

Recommended treatments
Interior:

  • 1 x Amotherm Steel Primer Epoxy SB on galvanised structures / 1x Amotherm Steel Primer SB on black iron
  • Amotherm Steel SB in multiple coats to reach the prescribed quantity
  • 1 x Amotherm Steel Top SB (optional for coloured finishes)

Outdoors (semi-exposed):

  • 1 x Amotherm Steel Primer Epoxy SB on galvanised structures / 1x Amotherm Steel Primer SB on black iron
  • Amotherm Steel SB in multiple coats to reach the prescribed quantity
  • 1 x Amotherm Steel Top SB

 

Packaging

10 – 5 Kg

 

Certifications

Certified for the purposes of European technical assessment ETA 15 / 0303

 
 